Welder Qualification Test Record
Qualification
Welder
Welder
WPS
TX-ED-WP1 Rev. 4
TX-ED-WP1 Rev. 4
PQR
TX-PQ-SM-02
TX-PQ-SM-02
Description of Variable
Values
Used in Test
Used in Test
Permitted Qualifications
Weld Process
SMAW- 6010 Root, 7018 Balance
SMAW- 6010 Root, 7018 Balance
Weld Current & Polarity
DCEP
AC or DC
Weld Position
3G
1F,2F,3F,1G,2G,3G
Weld Progression
Up
Up
Weld Backing Used
None
With or without backing
Material Type (spec)
A-36 Steel
Any M-1 material
Plate - Groove
3/8"
1/8" to 3/4"
Plate - Fillet
N/A
1/8" to Unlimited
Pipe Wall - Groove
N/A
1/8" to 3/4"
Pipe Wall - Fillet
N/A
1/8" to Unlimited
Pipe Outside - Groove
N/A
> 24" Only
Pipe Outside - Fillet
N/A
All pipe fillets
Weld deposit thickness
1/8" (.120 in)
1/8" per pass
Filler Metal - Spec #
AWS A5.1
AWS 5.1
Filler Metal - Class #
E6010/E7018
E70XX, E60XX
Filler Metal - F #
F-3/4
F-1 to 4
GTAW - Spec #
N/A
N/A
GTAW - Class #
N/A
N/A
Shielding & Gas Comp.
N/A
N/A
Visual Inspection
- Acceptable: Yes
- Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
- Film ID #'s: N/A
Guided Bend Test
- Face Bends Acceptable: Acceptable
- Root Bends Acceptable: Acceptable
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
- Weld Appearance: N/A
- Fillet Weld Size: N/A
- Fractured Root: N/A
- Cross Section: N/A
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D1.1: 2015 Structural Steel Welding Code.
Approved By
Richard J DePue
Richard J DePue
Organization
CWT Co.
CWT Co.
Qualifications
SCWI, Test Supervisor
SCWI, Test Supervisor
License
#03010018
#03010018
Supplementary Information
- Welders are only qualified to weld on the thicknesses and diameters listed above.
- Welders are only qualified to weld in the positions listed above.
- Qualification on groove welds will qualify a welder to make groove and fillet welds.
- Qualification of fillet welds will only qualify a welder to make fillet welds.
- Welders are only qualified to weld the types of metals listed.
- A welder must be able to produce their updated log sheet anytime their certification is questioned.
- Structural welders are not qualified to make welds on pressurized components.
- Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
- Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
- Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
- A welder is only qualified to use the electrodes identified above.
- Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
- Must be stored in a heated vented oven at 250°F.
- Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
- Must be purchased in a sealed container.
- Cannot be used if damaged or wet.
- All other electrodes:
- Must be kept dry.
- Cannot be used if damaged or wet.
- Should not be stored in an electrode oven with low hydrogen electrodes.
- For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.
Samuel Olson
Technology Exploration and Career Center West
ID #
519-12031951
519-12031951
Witness
Michael DePauw
Michael DePauw
Tested
May 07, 2021
May 07, 2021
Certified
May 10, 2021
May 10, 2021
Welder Qualification Test Record
Qualification
Welder
Welder
WPS
TX-ED-WP2 Rev. 4
TX-ED-WP2 Rev. 4
PQR
TX-PQ-FC-02
TX-PQ-FC-02
Description of Variable
Values
Used in Test
Used in Test
Permitted Qualifications
Weld Process
FCAW
FCAW
Weld Current & Polarity
DCEP
DCEP
Weld Position
2F
1F, 2F
Weld Progression
N/A
N/A
Weld Backing Used
N/A
N/A
Material Type (spec)
A-36 Steel
Any M-1 material
Plate - Groove
N/A
N/A
Plate - Fillet
3/8"
1/8" to 3/8"
Pipe Wall - Groove
N/A
N/A
Pipe Wall - Fillet
N/A
1/8 to 3/8"
Pipe Outside - Groove
N/A
N/A
Pipe Outside - Fillet
N/A
All pipe fillets
Weld deposit thickness
Single and Multi-Pass Fillets
Single and Multi-Pass Fillets
Filler Metal - Spec #
AWS A5.20
AWS 5.20
Filler Metal - Class #
E71T-1
E71T-X
Filler Metal - F #
F-6
F-6
GTAW - Spec #
N/A
N/A
GTAW - Class #
N/A
N/A
Shielding & Gas Comp.
Ar/CO2
Ar/CO2
Visual Inspection
- Acceptable: Yes
- Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
- Film ID #'s: N/A
Guided Bend Test
- Face Bends Acceptable: N/A
- Root Bends Acceptable: N/A
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
- Weld Appearance: Acceptable
- Fillet Weld Size: 5/16"
- Fractured Root: Acceptable
- Cross Section: Acceptable
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D1.1: 2015 Structural Steel Welding Code.
Approved By
Richard J DePue
Richard J DePue
Organization
CWT Co.
CWT Co.
Qualifications
SCWI, Test Supervisor
SCWI, Test Supervisor
License
#03010018
#03010018
Supplementary Information
- Welders are only qualified to weld on the thicknesses and diameters listed above.
- Welders are only qualified to weld in the positions listed above.
- Qualification on groove welds will qualify a welder to make groove and fillet welds.
- Qualification of fillet welds will only qualify a welder to make fillet welds.
- Welders are only qualified to weld the types of metals listed.
- A welder must be able to produce their updated log sheet anytime their certification is questioned.
- Structural welders are not qualified to make welds on pressurized components.
- Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
- Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
- Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
- A welder is only qualified to use the electrodes identified above.
- Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
- Must be stored in a heated vented oven at 250°F.
- Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
- Must be purchased in a sealed container.
- Cannot be used if damaged or wet.
- All other electrodes:
- Must be kept dry.
- Cannot be used if damaged or wet.
- Should not be stored in an electrode oven with low hydrogen electrodes.
- For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.
Samuel Olson
Technology Exploration and Career Center West
ID #
519-12031951
519-12031951
Witness
Michael DePauw
Michael DePauw
Tested
May 07, 2021
May 07, 2021
Certified
May 10, 2021
May 10, 2021
Welder Qualification Test Record
Qualification
Welder
Welder
WPS
TX-ED-WP7 Rev. 4
TX-ED-WP7 Rev. 4
PQR
TX-PQ-GM-01
TX-PQ-GM-01
Description of Variable
Values
Used in Test
Used in Test
Permitted Qualifications
Weld Process
GMAW-G
GMAW- G, SP
Weld Current & Polarity
DCEP
DCEP
Weld Position
3G
1F,2F,3F,1G,2G,3G
Weld Progression
N/A
N/A
Weld Backing Used
None
With or without backing
Material Type (spec)
A-36 Steel
Any M-1 material
Plate - Groove
3/8"
1/8" to 3/4"
Plate - Fillet
N/A
1/8" to Unlimited
Pipe Wall - Groove
N/A
1/8" to 3/4"
Pipe Wall - Fillet
N/A
1/8" to Unlimited
Pipe Outside - Groove
N/A
> 24" Only
Pipe Outside - Fillet
N/A
All pipe fillets
Weld deposit thickness
1/8" per pass
1/8" per pass
Filler Metal - Spec #
AWS A5.18
AWS 5.18
Filler Metal - Class #
ER70S-6
ER70S-X
Filler Metal - F #
F-6
F-6
GTAW - Spec #
N/A
N/A
GTAW - Class #
N/A
N/A
Shielding & Gas Comp.
Ar/CO2
Ar/CO2
Visual Inspection
- Acceptable: Yes
- Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
- Film ID #'s: N/A
Guided Bend Test
- Face Bends Acceptable: Acceptable
- Root Bends Acceptable: Acceptable
- Side Bends Acceptable: N/A
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
- Weld Appearance: N/A
- Fillet Weld Size: N/A
- Fractured Root: N/A
- Cross Section: N/A
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D1.1: 2015 Structural Steel Welding Code.
Approved By
Richard J DePue
Richard J DePue
Organization
CWT Co.
CWT Co.
Qualifications
SCWI, Test Supervisor
SCWI, Test Supervisor
License
#03010018
#03010018
Supplementary Information
- Welders are only qualified to weld on the thicknesses and diameters listed above.
- Welders are only qualified to weld in the positions listed above.
- Qualification on groove welds will qualify a welder to make groove and fillet welds.
- Qualification of fillet welds will only qualify a welder to make fillet welds.
- Welders are only qualified to weld the types of metals listed.
- A welder must be able to produce their updated log sheet anytime their certification is questioned.
- Structural welders are not qualified to make welds on pressurized components.
- Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
- Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
- Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
- A welder is only qualified to use the electrodes identified above.
- Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
- Must be stored in a heated vented oven at 250°F.
- Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
- Must be purchased in a sealed container.
- Cannot be used if damaged or wet.
- All other electrodes:
- Must be kept dry.
- Cannot be used if damaged or wet.
- Should not be stored in an electrode oven with low hydrogen electrodes.
- For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.
Samuel Olson
Technology Exploration and Career Center West
ID #
519-12031951
519-12031951
Witness
Michael DePauw
Michael DePauw
Tested
December 16, 2020
December 16, 2020
Certified
January 15, 2021
January 15, 2021
Welder Qualification Test Record
Qualification
Welder
Welder
WPS
TX-ED-WP6 Rev. 4
TX-ED-WP6 Rev. 4
PQR
TX-PQ-GT-01
TX-PQ-GT-01
Description of Variable
Values
Used in Test
Used in Test
Permitted Qualifications
Weld Process
GTAW
GTAW
Weld Current & Polarity
DCEN
DCEN
Weld Position
1G
1F, 2F, 1G
Weld Progression
N/A
N/A
Weld Backing Used
None
With or without Backing
Material Type (spec)
A-36 Steel
Any M-1 material
Plate - Groove
3/8"
1/8" to 3/4"
Plate - Fillet
N/A
1/8" to Unlimited
Pipe Wall - Groove
N/A
1/8" to 3/4"
Pipe Wall - Fillet
N/A
1/8" to Unlimited
Pipe Outside - Groove
N/A
> 24" Only
Pipe Outside - Fillet
N/A
All pipe fillets
Weld deposit thickness
1/8" per pass
1/8" Max per pass
Filler Metal - Spec #
AWS A5.18
AWS 5.18
Filler Metal - Class #
ER70S-2
ER70S-X
Filler Metal - F #
F-6
F-6
GTAW - Spec #
A5.12
A5.12
GTAW - Class #
EWTh-2
EWTH-2
Shielding & Gas Comp.
Argon
Argon
Visual Inspection
- Acceptable: Yes
- Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
- Film ID #'s: N/A
Guided Bend Test
- Face Bends Acceptable: Acceptable
- Root Bends Acceptable: Acceptable
- Side Bends Acceptable: N/A
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
- Weld Appearance: N/A
- Fillet Weld Size: N/A
- Fractured Root: N/A
- Cross Section: N/A
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D1.1: 2015 Structural Steel Welding Code.
Approved By
Richard J DePue
Richard J DePue
Organization
CWT Co.
CWT Co.
Qualifications
SCWI, Test Supervisor
SCWI, Test Supervisor
License
#03010018
#03010018
Supplementary Information
- Welders are only qualified to weld on the thicknesses and diameters listed above.
- Welders are only qualified to weld in the positions listed above.
- Qualification on groove welds will qualify a welder to make groove and fillet welds.
- Qualification of fillet welds will only qualify a welder to make fillet welds.
- Welders are only qualified to weld the types of metals listed.
- A welder must be able to produce their updated log sheet anytime their certification is questioned.
- Structural welders are not qualified to make welds on pressurized components.
- Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
- Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
- Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
- A welder is only qualified to use the electrodes identified above.
- Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
- Must be stored in a heated vented oven at 250°F.
- Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
- Must be purchased in a sealed container.
- Cannot be used if damaged or wet.
- All other electrodes:
- Must be kept dry.
- Cannot be used if damaged or wet.
- Should not be stored in an electrode oven with low hydrogen electrodes.
- For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.
Samuel Olson
Technology Exploration and Career Center West
ID #
519-12031951
519-12031951
Witness
Michael DePauw
Michael DePauw
Tested
November 18, 2020
November 18, 2020
Certified
December 09, 2020
December 09, 2020
Welder Qualification Test Record
Qualification
ASME Welder
ASME Welder
WPS
NWG-WPS-CS-GTAW-01
NWG-WPS-CS-GTAW-01
PQR
NWG-PQR-CS-GTAW-01
NWG-PQR-CS-GTAW-01
Description of Variable
Values
Used in Test
Used in Test
Permitted Qualifications
Weld Process
GTAW
GTAW
Weld Current & Polarity
DCEN
DCEN
Weld Position
1F
1F
Weld Progression
N/A
N/A
Weld Backing Used
N/A
N/A
Material Type (QW-403)
P-No. 1
*P1 to P11, P41 to 49, P34
Plate - Groove
N/A
N/A
Plate - Fillet
3/8"
Unlimited
Pipe Wall - Groove
N/A
N/A
Pipe Wall - Fillet
N/A
Unlimited
Pipe Outside - Groove
N/A
N/A
Pipe Outside - Fillet
N/A
All pipe fillets
Weld deposit thickness
Single pass
Single and multi-pass fillets
Filler Metal - Spec #
AWS A5.18
AWS A5.18
Filler Metal - Class #
ER70S-2
ER70S-X
Filler Metal - F #
F-6
F-6
GTAW - Spec #
A5.12
A5.12
GTAW - Class #
EWTh-2
EWTh-2
Shielding & Gas Comp.
Argon
Argon
Visual Inspection
- Acceptable: Yes, QW-194
- Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
- Film ID #'s: N/A
Guided Bend Test
- Face Bends Acceptable: N/A
- Root Bends Acceptable: N/A
- Side Bends Acceptable: N/A
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
- Weld Appearance: Acceptable, QW-194
- Fillet Weld Size: 1/4"
- Fractured Root: Acceptable, QW-462
- Cross Section: Acceptable, QW-462
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of ASME BPV Welding Code, Section IX.
Approved By
Richard J DePue
Richard J DePue
Organization
CWT Co.
CWT Co.
Qualifications
SCWI, Test Supervisor
SCWI, Test Supervisor
License
#03010018
#03010018
Supplementary Information
- Welders are only qualified to weld on the thicknesses and diameters listed above.
- Welders are only qualified to weld in the positions listed above.
- Qualification on groove welds will qualify a welder to make groove and fillet welds.
- Qualification of fillet welds will only qualify a welder to make fillet welds.
- Welders are only qualified to weld the types of metals listed.
- A welder must be able to produce their updated log sheet anytime their certification is questioned.
- This qualification permits welding on structural and/or/pressurized components.
- Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
- Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
- Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
- A welder is only qualified to use the electrodes identified above.
- Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
- Must be stored in a heated vented oven at 250°F.
- Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
- Must be purchased in a sealed container.
- Cannot be used if damaged or wet.
- All other electrodes:
- Must be kept dry.
- Cannot be used if damaged or wet.
- Should not be stored in an electrode oven with low hydrogen electrodes.
- For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.
Samuel Olson
Technology Exploration and Career Center West
ID #
519-12031951
519-12031951
Witness
Michael DePauw
Michael DePauw
Tested
November 09, 2020
November 09, 2020
Certified
November 16, 2020
November 16, 2020
Welder Qualification Test Record
Qualification
Welder
Welder
WPS
TX-ED-WP7 Rev. 4
TX-ED-WP7 Rev. 4
PQR
TX-PQ-GM-03
TX-PQ-GM-03
Description of Variable
Values
Used in Test
Used in Test
Permitted Qualifications
Weld Process
GMAW-S
GMAW-S
Weld Current & Polarity
DCEP
DCEP
Weld Position
3F
1F, 2F, 3F
Weld Progression
Down
Down
Weld Backing Used
N/A
N/A
Material Type (spec)
A-36 Steel
Any M-1 material
Plate - Groove
N/A
N/A
Plate - Fillet
11ga (.120 in)
16ga (.062 in) to 3ga (.239 in)
Pipe Wall - Groove
N/A
N/A
Pipe Wall - Fillet
N/A
16ga (.062 in) to 3ga (.239 in)
Pipe Outside - Groove
N/A
N/A
Pipe Outside - Fillet
N/A
N/A
Weld deposit thickness
Single and Multi-pass
Both
Filler Metal - Spec #
AWS A5.18
AWS 5.18
Filler Metal - Class #
ER70S-6
ER70S-X
Filler Metal - F #
F-6
F-6
GTAW - Spec #
N/A
N/A
GTAW - Class #
N/A
N/A
Shielding & Gas Comp.
Ar/CO2
Ar/CO2
Visual Inspection
- Acceptable: Yes
- Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
- Film ID #'s: N/A
Guided Bend Test
- Face Bends Acceptable: N/A
- Root Bends Acceptable: N/A
- Side Bends Acceptable: N/A
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
- Weld Appearance: N/A
- Fillet Weld Size: N/A
- Fractured Root: N/A
- Cross Section: N/A
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D9.1: 2012 Sheet Metal Welding Code.
Approved By
Richard J DePue
Richard J DePue
Organization
CWT Co.
CWT Co.
Qualifications
SCWI, Test Supervisor
SCWI, Test Supervisor
License
#03010018
#03010018
Supplementary Information
- Welders are only qualified to weld on the thicknesses and diameters listed above.
- Welders are only qualified to weld in the positions listed above.
- Qualification on groove welds will qualify a welder to make groove and fillet welds.
- Qualification of fillet welds will only qualify a welder to make fillet welds.
- Welders are only qualified to weld the types of metals listed.
- A welder must be able to produce their updated log sheet anytime their certification is questioned.
- Structural welders are not qualified to make welds on pressurized components.
- Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
- Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
- Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
- A welder is only qualified to use the electrodes identified above.
- Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
- Must be stored in a heated vented oven at 250°F.
- Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
- Must be purchased in a sealed container.
- Cannot be used if damaged or wet.
- All other electrodes:
- Must be kept dry.
- Cannot be used if damaged or wet.
- Should not be stored in an electrode oven with low hydrogen electrodes.
- For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.
Samuel Olson
Technology Exploration and Career Center West
ID #
519-12031951
519-12031951
Witness
Michael DePauw
Michael DePauw
Tested
November 05, 2020
November 05, 2020
Certified
November 16, 2020
November 16, 2020
Welder Qualification Test Record
Qualification
Welder
Welder
WPS
TX-ED-WP1 Rev. 4
TX-ED-WP1 Rev. 4
PQR
TX-PQ-SM-01
TX-PQ-SM-01
Description of Variable
Values
Used in Test
Used in Test
Permitted Qualifications
Weld Process
SMAW
SMAW
Weld Current & Polarity
DCEP
AC or DC
Weld Position
4F
1F, 2F, 4F
Weld Progression
N/A
N/A
Weld Backing Used
N/A
N/A
Material Type (spec)
A-36 Steel
Any M-1 material
Plate - Groove
N/A
N/A
Plate - Fillet
3/8"
1/8" to 3/8"
Pipe Wall - Groove
N/A
N/A
Pipe Wall - Fillet
N/A
1/8" to 3/8"
Pipe Outside - Groove
N/A
N/A
Pipe Outside - Fillet
N/A
All pipe fillets
Weld deposit thickness
Single and Multi-Pass Fillets
Single and Multi-Pass Fillets
Filler Metal - Spec #
AWS A5.1
AWS 5.1
Filler Metal - Class #
E7018
E70XX, E60XX
Filler Metal - F #
F-4
F-1 to 4
GTAW - Spec #
N/A
N/A
GTAW - Class #
N/A
N/A
Shielding & Gas Comp.
N/A
N/A
Visual Inspection
- Acceptable: Yes
- Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
- Film ID #'s: N/A
Guided Bend Test
- Face Bends Acceptable: N/A
- Root Bends Acceptable: N/A
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
- Weld Appearance: Acceptable
- Fillet Weld Size: 5/16"
- Fractured Root: Acceptable
- Cross Section: Acceptable
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D1.1: 2015 Structural Steel Welding Code.
Approved By
Richard J DePue
Richard J DePue
Organization
CWT Co.
CWT Co.
Qualifications
SCWI, Test Supervisor
SCWI, Test Supervisor
License
#03010018
#03010018
Supplementary Information
- Welders are only qualified to weld on the thicknesses and diameters listed above.
- Welders are only qualified to weld in the positions listed above.
- Qualification on groove welds will qualify a welder to make groove and fillet welds.
- Qualification of fillet welds will only qualify a welder to make fillet welds.
- Welders are only qualified to weld the types of metals listed.
- A welder must be able to produce their updated log sheet anytime their certification is questioned.
- Structural welders are not qualified to make welds on pressurized components.
- Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
- Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
- Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
- A welder is only qualified to use the electrodes identified above.
- Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
- Must be stored in a heated vented oven at 250°F.
- Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
- Must be purchased in a sealed container.
- Cannot be used if damaged or wet.
- All other electrodes:
- Must be kept dry.
- Cannot be used if damaged or wet.
- Should not be stored in an electrode oven with low hydrogen electrodes.
- For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.