Welder Qualification Test Record

Qualification Type
Welder

WPS
TX-ED-WP7 Rev. 4
PQR
TX-PQ-GM-03


Description of Variable

Actual Values
Used in Weld Test
Permitted Qualifications Range

Welding Process
GMAW-S
GMAW-S
Welding Current & Polarity
DCEP
DCEP
Welding Position
2F
1F, 2F
Welding Progression (up or down)
N/A
N/A
Weld Backing Used (grooves)
N/A
N/A
Material Type (specification)
A-36 Steel
Any M-1 material
Plate Thickness - Groove
N/A
N/A
Plate Thickness - Fillet
11ga (.120 in)
16ga (.062 in) to 3ga (.239 in)
Pipe Wall Thickness - Groove
N/A
N/A
Pipe Wall Thickness - Fillet
N/A
16ga (.062 in) to 3ga (.239 in)
Pipe Outside Diameter - Groove
N/A
N/A
Pipe Outside Diameter - Fillet
N/A
All pipe fillets
Weld deposit thickness
Single and Multi-pass
Both
Filler Metal - Specification #
AWS A5.18
AWS 5.18
Filler Metal - Classification #
ER70S-6
ER70S-X
Filler Metal - F #
F-6
F-6
GTAW Electrode - Specification #
N/A
N/A
GTAW Electrode - Classification #
N/A
N/A
Shielding & Gas Composition.
Ar/CO2
Ar/CO2
Visual Inspection
  • Acceptable: Yes
  • Procedure: IW-VT-01, Rev. 2, 07-25-12
*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.
Radiographic Test
  • Film ID #'s: N/A
Guided Bend Test
  • Face Bends Acceptable: N/A
  • Root Bends Acceptable: N/A
  • Side Bends Acceptable: N/A
*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.
Fillet Break Test
  • Weld Appearance: N/A
  • Fillet Weld Size: N/A
  • Fractured Root: N/A
  • Cross Section: N/A
*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.
The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D9.1: 2012 Sheet Metal Welding Code.
Approved By
Richard J DePue
Organization
CWT Co.
Qualifications
SCWI, Test Supervisor
License Stamp
License
#03010018

Supplementary Information

  1. Welders are only qualified to weld on the thicknesses and diameters listed above.
  2. Welders are only qualified to weld in the positions listed above.
  3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
  4. Qualification of fillet welds will only qualify a welder to make fillet welds.
  5. Welders are only qualified to weld the types of metals listed.
  6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
  7. Structural welders are not qualified to make welds on pressurized components.
  8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
  9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
  10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
  11. A welder is only qualified to use the electrodes identified above.
  12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
  13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
  14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.