Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
James Saccomanno

Tested
May 16, 2024

Certified
June 07, 2024

Welder Qualification Test Record

Qualification Type
API 1104 Single Welder Qualification

WPS
AWS 1-GTAW

PQR
AWS 1 GTAW PQ

Qualification Test Performed

Welding Process, Electrode, Group

GTAW, EWTh-2

Method of Application

Manual

Pipe Material and Grade

ASTM A53, (X52)

Diameter and Wall Thickness

4.5 in. OD, .355 in. Wall

Joint Type and Design

Weld Pipe Butt Joint 1G, Rotated

Welding Position

Rotated

Polarity, Shielding Gas

DCEN

Essential Variables Qualified By Test

Types of Base Metal Qualified

Group B, X42, X52

Welding Process, Electrode Qualified

GTAW

Welding Current Qualified for Use

DCEN

Production Positions Qualified For Use

1G, 1F, 2F, Rotated

Wall Thickness Group Qualified For Use

Group 2, 0.188 in. to 0.355 in.

Diameter Group Qualified For Use

Group 2, 2.375 in. to 4.5 in. 0D

Visual Inspection Results

weld Profile and Appearance

Acceptable, 6.4

Complete Weld Joint Fusion

Root Bend Straps- Acceptable - 2 ea.

Fillet Weld Nick Break Testing

Groove Nick Breaks Acceptable - 2 ea.

Porosity located in the weld is < 1/16in.

Acceptable

Undercut is less than < 1/32 in.

Acceptable

Slag Inclusions

Acceptable

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of API 1104, 20th Ed., Standard For Welding Pipelines and Related Facilities.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
AWS, API, SCWI

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
James Saccomanno

Tested
May 16, 2024

Certified
June 07, 2024

Welder Qualification Test Record

Qualification Type
API 1104 Single Welder Qualification

WPS
CWT GW001

PQR
CWT GWPQ1

Qualification Test Performed

Welding Process, Electrode, Group

SMAW- 6010 Root, 7018 Balance

Method of Application

Manual

Pipe Material and Grade

ASTM A53, (X52)

Diameter and Wall Thickness

4.5 in. OD, .355 in. Wall

Joint Type and Design

Weld Pipe Butt Joint 5G, 6G, Fixed

Welding Position

Fixed Position

Polarity, Shielding Gas

DCEP

Essential Variables Qualified By Test

Types of Base Metal Qualified

Group B, X42, X52

Welding Process, Electrode Qualified

SMAW - Electrode Groups 1, 3

Welding Current Qualified for Use

DCEP

Production Positions Qualified For Use

All Butt Joint and Fillet Positions

Wall Thickness Group Qualified For Use

Group 2, 0.188 in. to 0.355 in.

Diameter Group Qualified For Use

Group 2, 2.375 in. to 4.5 in. 0D

Visual Inspection Results

weld Profile and Appearance

Acceptable, 6.4

Complete Weld Joint Fusion

Root Bend Straps- Acceptable - 2 ea.

Fillet Weld Nick Break Testing

Groove Nick Breaks Acceptable - 2 ea.

Porosity located in the weld is < 1/16in.

Acceptable

Undercut is less than < 1/32 in.

Acceptable

Slag Inclusions

Acceptable

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of API 1104, 20th Ed., Standard For Welding Pipelines and Related Facilities.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
AWS, API, SCWI

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
James Saccomanno

Tested
February 29, 2024

Certified
March 21, 2024

Welder Qualification Test Record

Qualification Type
API 1104 Welder Qualification - Single

WPS
CWT GW001

PQR
CWT GWPQ1

Qualification Test Performed

Welding Process, Electrode, Group

SMAW, E6010 Root, 7018 Out

Method of Application

Manual

Pipe Material and Grade

ASTM A53, (X52)

Diameter and Wall Thickness

4 in. OD, .337 in. Wall

Joint Type and Design

Pipe Single V Butt Joint, Fixed

Welding Position

2G Fixed

Polarity, Shielding Gas

DCEP

Essential Variables Qualified By Test

Types of Base Metal Qualified

Group B, X42, X52

Welding Process, Electrode Qualified

SMAW - Electrode Groups 1, 3

Welding Current Qualified for Use

DCEP

Production Positions Qualified For Use

1G, 2G Pipe Butt Joints, Fixed and Rolled

Wall Thickness Group Qualified For Use

Group 2, 0.188 in. to 0.337 in.

Diameter Group Qualified For Use

Group 2, 2.375 in. to 4 in. 0D

Visual Inspection Results

weld Profile and Appearance

Acceptable, 6.4

Complete Weld Joint Fusion

Face and Root Bend Straps- Acceptable

Fillet Weld Nick Break Testing

Nick Breaks Acceptable

Porosity located in the weld is < 1/16in.

Acceptable

Undercut is less than < 1/32 in.

Acceptable

Slag Inclusions

Acceptable

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of API 1104, 20th Ed., Standard For Welding Pipelines and Related Facilities.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
AWS, API, SCWI

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
James Saccomanno

Tested
February 29, 2024

Certified
March 04, 2024

Welder Qualification Test Record

Qualification Type
Welder

WPS
TX-ED-WP1 Rev. 4

PQR
TX-PQ-SM-02

Description of Variable

Actual Values
Used in Weld Test

Permitted Qualifications Range

Welding Process

SMAW- 6010 Root, 7018 Cap/Fill

SMAW- 6010 Root, 7018 Cap/Fill

Welding Current & Polarity

DCEP

AC or DC

Welding Position

3G, 4G

All Position Plate

Welding Progression (up or down)

Up

Up

Weld Backing Used (grooves)

None

With or without backing

Material Type (specification)

A-36 Steel

Any M-1 material

Plate Thickness - Groove

3/8"

1/8" to 3/4"

Plate Thickness - Fillet

N/A

1/8" to Unlimited

Pipe Wall Thickness - Groove

N/A

1/8" to 3/4"

Pipe Wall Thickness - Fillet

N/A

1/8" to Unlimited

Pipe Outside Diameter - Groove

N/A

> 24" Only

Pipe Outside Diameter - Fillet

N/A

All pipe fillets

Weld deposit thickness

1/8" per pass

1/8" per pass

Filler Metal - Specification #

AWS A5.1

AWS 5.1

Filler Metal - Classification #

E6010/E7018

E60XX,E70XX

Filler Metal - F #

F-3,4

F-1 to 4

GTAW Electrode - Specification #

N/A

N/A

GTAW Electrode - Classification #

N/A

N/A

Shielding & Gas Composition.

N/A

N/A

Visual Inspection

• Acceptable: Yes
• Procedure: IW-VT-01, Rev. 2, 07-25-12

*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.

Radiographic Test

• Film ID #'s: N/A

Guided Bend Test

• Face Bends Acceptable: Acceptable
• Root Bends Acceptable: Acceptable

*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.

Fillet Break Test

• Weld Appearance: N/A
• Fillet Weld Size: N/A
• Fractured Root: N/A
• Cross Section: N/A

*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.

The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D1.1: 2015 Structural Steel Welding Code.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
SCWI, Test Supervisor

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
James Saccomanno

Tested
February 29, 2024

Certified
March 04, 2024

Welder Qualification Test Record

Qualification Type
AWS D9.1 Welder Qualification

WPS
WPS-EDU6-SS

PQR
PQR-EDU6-SS

Qualification Test Performed

> 70% Score Written Knowledge Test

Not Reported

Welding Process and Electrode Tested with

GTAW, EWTh-2

Metal Type/Condition

Sheet Stainless Steel to Sheet Stainless Steel

Groove Weld Test Position/Backing

N/A

Fillet Weld Test Position

3F Up

Test Metal Thickness

3 Ga. (0.239 in.)

Shielding Gas

Argon

Essential Variables Qualified By Test

Types of Base Metal Qualified

Sheet to Sheet or Structural Stainless Steel

Welding Process Qualified

GTAW

Filler Metal F-Number Qualified

F-6

Welding Current Qualified for Use

DCEN

Production Positions Qualified For Use

1F, 2F, 3FUp &Down

Metal Thickness Range Qualified For Use

11 ga. (0.120 in.) to 3 ga. (0.239 in.)

Visual Inspection Results

Complete Weld Joint Fusion and Penetration

Acceptable

Groove Weld Face Reinforcement < 1/8 in.

N/A

Required minimum throat size

Acceptable

Weld convexity < 1/8 in.

Acceptable

Porosity located in the weld is < 1/32 in.

Acceptable*

Undercut is less than < 1/32 in.

Acceptable*

Base Metal, Weld, HAZ, cracking

Acceptable

 

*Based on min. 1/8 in. metal thickness

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of AWS D9.1 Sheet Metal Welding Code.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
SCWI, Test Supervisor

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
James Saccomanno

Tested
February 29, 2024

Certified
March 04, 2024

Welder Qualification Test Record

Qualification Type
AWS D9.1 Welder Qualification

WPS
WPS-EDU6

PQR
PQR-EDU6

Qualification Test Performed

> 70% Score Written Knowledge Test

Not Reported

Welding Process and Electrode Tested with

GTAW, EWTh-2

Metal Type/Condition

Sheet Steel to Sheet Steel Uncoated

Groove Weld Test Position/Backing

N/A

Fillet Weld Test Position

1F, 2F ,3F Up, 4F

Test Metal Thickness

3 Ga. (0.239 in.)

Shielding Gas

Argon

Essential Variables Qualified By Test

Types of Base Metal Qualified

Sheet Steel to Sheet or Structural Steel

Welding Process Qualified

GTAW

Filler Metal F-Number Qualified

F-6

Welding Current Qualified for Use

DCEN

Production Positions Qualified For Use

1F, 2F, 3FUp &Down, 4F

Metal Thickness Range Qualified For Use

11 ga. (0.120 in.) to 3 ga. (0.239 in.)

Visual Inspection Results

Complete Weld Joint Fusion and Penetration

Acceptable

Groove Weld Face Reinforcement < 1/8 in.

N/A

Required minimum throat size

Acceptable

Weld convexity < 1/8 in.

Acceptable

Porosity located in the weld is < 1/32 in.

Acceptable*

Undercut is less than < 1/32 in.

Acceptable*

Base Metal, Weld, HAZ, cracking

Acceptable

 

*Based on min. 1/8 in. metal thickness

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of AWS D9.1 Sheet Metal Welding Code.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
SCWI, Test Supervisor

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
James Saccomanno

Tested
February 29, 2024

Certified
March 04, 2024

Welder Qualification Test Record

Qualification Type
AWS D9.1 Welder Qualification

WPS
WPS-EDU6-SS

PQR
PQR-EDU6-SS

Qualification Test Performed

> 70% Score Written Knowledge Test

Not Reported

Welding Process and Electrode Tested with

GTAW, EWTh-2

Metal Type/Condition

Sheet Stainless Steel to Sheet Stainless Steel

Groove Weld Test Position/Backing

1G without Back Weld

Fillet Weld Test Position

N/A

Test Metal Thickness

3 Ga. (0.239 in.)

Shielding Gas

Argon

Essential Variables Qualified By Test

Types of Base Metal Qualified

Sheet to Sheet or Structural Stainless Steel

Welding Process Qualified

GTAW

Filler Metal F-Number Qualified

F-6

Welding Current Qualified for Use

DCEP

Production Positions Qualified For Use

1F, 2F, 1G With or without Backing or Backweld

Metal Thickness Range Qualified For Use

11 ga. (0.120 in.) to 3 ga. (0.239 in.)

Visual Inspection Results

Complete Weld Joint Fusion and Penetration

Acceptable

Groove Weld Face Reinforcement < 1/8 in.

Acceptable

Required minimum throat size

Acceptable

Weld convexity < 1/8 in.

N/A

Porosity located in the weld is < 1/32 in.

Acceptable*

Undercut is less than < 1/32 in.

Acceptable*

Base Metal, Weld, HAZ, cracking

Acceptable

 

*Based on min. 1/8 in. metal thickness

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of AWS D9.1 Sheet Metal Welding Code.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
SCWI, Test Supervisor

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
Louis Doak

Tested
February 23, 2023

Certified
May 10, 2023

Welder Qualification Test Record

Qualification Type
AWS D9.1 Welder Qualification

WPS
ANSI/AWS B2.1-1-016-94

PQR
Prequalified

Qualification Test Performed

> 70% Score Written Knowledge Test

Not Reported

Welding Process and Electrode Tested with

SMAW- E7018

Metal Type/Condition

Steel, Uncoated

Groove Weld Test Position/Backing

N/A

Fillet Weld Test Position

1F, 2F, 3F Up, 4F

Test Metal Thickness

3 Ga. (0.239 in.)

Shielding Gas

N/A

Essential Variables Qualified By Test

Types of Base Metal Qualified

Uncoated Steel < 0.30% C, 0.50% Cr

Welding Process Qualified

SMAW- Manual

Filler Metal F-Number Qualified

F-4

Welding Current Qualified for Use

DCEP

Production Positions Qualified For Use

1F, 2F, 3F Up & Down, 4F

Metal Thickness Range Qualified For Use

11 ga. (0.120 in.) to 3 ga. (0.239 in.)

Visual Inspection Results

Complete Weld Joint Fusion and Penetration

Acceptable

Groove Weld Face Reinforcement < 1/8 in.

N/A

Required minimum throat size

Acceptable

Weld convexity < 1/8 in.

Acceptable

Porosity located in the weld is < 1/32 in.

Acceptable*

Undercut is less than < 1/32 in.

Acceptable*

Base Metal, Weld, HAZ, cracking

Acceptable

 

*Based on min. 1/8 in. metal thickness

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of AWS D9.1 Sheet Metal Welding Code.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
SCWI, Test Supervisor

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
Louis Doak

Tested
April 27, 2023

Certified
May 09, 2023

Welder Qualification Test Record

Qualification Type
Welder

WPS
TX-ED-WP1 Rev. 4

PQR
TX-PQ-SM-02

Description of Variable

Actual Values
Used in Weld Test

Permitted Qualifications Range

Welding Process

SMAW

SMAW

Welding Current & Polarity

DCEP

AC or DC

Welding Position

1G, 2G

1F,2F,1G, 2G

Welding Progression (up or down)

N/A

N/A

Weld Backing Used (grooves)

None

With or W/out Backing

Material Type (specification)

A-36 Steel

Any M-1 material

Plate Thickness - Groove

3/8"

1/8" to 3/4"

Plate Thickness - Fillet

N/A

1/8" to Unlimited

Pipe Wall Thickness - Groove

N/A

1/8" to 3/4"

Pipe Wall Thickness - Fillet

N/A

1/8" to Unlimited

Pipe Outside Diameter - Groove

N/A

> 24" Only

Pipe Outside Diameter - Fillet

N/A

All pipe fillets

Weld deposit thickness

1/8" per pass

1/8" per pass

Filler Metal - Specification #

AWS A5.1

AWS 5.1

Filler Metal - Classification #

E7018

E70XX, E60XX

Filler Metal - F #

F-4

F-1 to 4

GTAW Electrode - Specification #

N/A

N/A

GTAW Electrode - Classification #

N/A

N/A

Shielding & Gas Composition.

N/A

N/A

Visual Inspection

• Acceptable: Yes
• Procedure: IW-VT-01, Rev. 2, 07-25-12

*Note - Visual inspection shall be in the "as welded" condition. See D1.1 and 4.81.

Radiographic Test

• Film ID #'s: N/A

Guided Bend Test

• Face Bends Acceptable: Acceptable
• Root Bends Acceptable: Acceptable

*Note - Bend specimens shall have all reinforcements removed. See D1.1 and 4.30.1.

Fillet Break Test

• Weld Appearance: N/A
• Fillet Weld Size: N/A
• Fractured Root: N/A
• Cross Section: N/A

*Note - For inspection and disposition of the fractured weld root see D1.1, 4.30.2.3 and 4.30.4.1.

The herein named authority, certifies that the statements in this record are correct and that the test welds were prepared, welded, and tested in conformance with the requirements of AWS D1.1: 2015 Structural Steel Welding Code.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
SCWI, Test Supervisor

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.

Owen Stoddard
Angleton ISD

ID #
006-436572

Witness
Louis Doak

Tested
October 12, 2022

Certified
December 20, 2022

Welder Qualification Test Record

Qualification Type
AWS D9.1 Welder Qualification

WPS
ANSI/AWS B2.1-1-016-94

PQR
Prequalified

Qualification Test Performed

> 70% Score Written Knowledge Test

Not Reported

Welding Process and Electrode Tested with

SMAW- E7018

Metal Type/Condition

Steel, Uncoated

Groove Weld Test Position/Backing

N/A

Fillet Weld Test Position

2F

Test Metal Thickness

3 Ga. (0.239 in.)

Shielding Gas

N/A

Essential Variables Qualified By Test

Types of Base Metal Qualified

Uncoated Steel < 0.30% C, 0.50% Cr

Welding Process Qualified

SMAW- Manual

Filler Metal F-Number Qualified

F-4

Welding Current Qualified for Use

DCEP

Production Positions Qualified For Use

1F, 2F

Metal Thickness Range Qualified For Use

11 ga. (0.120 in.) to 3 ga. (0.239 in.)

Visual Inspection Results

Complete Weld Joint Fusion and Penetration

Acceptable

Groove Weld Face Reinforcement < 1/8 in.

N/A

Required minimum throat size

Acceptable

Weld convexity < 1/8 in.

Acceptable

Porosity located in the weld is < 1/32 in.

Acceptable*

Undercut is less than < 1/32 in.

Acceptable*

Base Metal, Weld, HAZ, cracking

Acceptable

 

*Based on min. 1/8 in. metal thickness

We, the undersigned, certify that the statements in this record are correct and that the test welds were prepared, joined, and examined in accordance with the requirements of AWS D9.1 Sheet Metal Welding Code.

Approved By
Richard J DePue

Organization
CWT Co.

Qualifications
SCWI, Test Supervisor

License
#03010018

Supplementary Information

1. Welders are only qualified to weld on the thicknesses and diameters listed above.
2. Welders are only qualified to weld in the positions listed above.
3. Qualification on groove welds will qualify a welder to make groove and fillet welds.
4. Qualification of fillet welds will only qualify a welder to make fillet welds.
5. Welders are only qualified to weld the types of metals listed.
6. A welder must be able to produce their updated log sheet anytime their certification is questioned.
7. Structural welders are not qualified to make welds on pressurized components.
8. Always make sure base and filler metals are clean and free of slag, scale, rust, oil, paint or other foreign materials.
9. Oxy-fuel and plasma cut surfaces must be ground before welding to remove slag, oxides and heat affected zone.
10. Base metals shall be preheated when surface temperature is below 32°F and recommended when surface is below 70°F.
11. A welder is only qualified to use the electrodes identified above.
12. Low hydrogen electrodes, F-4 (7018 and any ending in 5, 6, 8):
    • Must be stored in a heated vented oven at 250°F.
    • Cannot be exposed to the atmosphere for time periods exceeding 4 hours.
    • Must be purchased in a sealed container.
    • Cannot be used if damaged or wet.
13. All other electrodes:
    • Must be kept dry.
    • Cannot be used if damaged or wet.
    • Should not be stored in an electrode oven with low hydrogen electrodes.
14. For AWS D1.1, ASME IX and API 1104 codes, a welder's qualification/certification will expire in 6 months unless continuity is demonstrated. An AWS D9.1 qualification will extend to 12 months. In all cases, if continuity is demonstrated using the process, qualification/certification will extend indefinitely.